*** LOW = H04 TS <
60 ksi; MEDIUM= H04 TS 60-75 ksi;
HIGH= H04 TS 76-100 ksi; VERY HIGH= H04 TS > 100 ksi
Performance
Levels: E = Excellent; G = Good; F =
Fair; P = Poor; NR = Not Recommended
|
Alloy UNS
or ACB # |
Composition |
Appearance (Color) |
Conductivity (Electrical & Thermal) % IACS |
Corrosion Resistance |
Cold Forming (Heading, Redrawing, Bending) |
Hot Forming (Forging) |
Joining (Solder) |
Joining (Braze) |
Joining (Arc Weld) |
Tensile Strength (Mechanical Properties) H04 *** |
Machining Machinability Rating FCB = 100 |
Wear Performance |
|
CuOFE CuOF CuETP |
COPPER |
99-102 |
HIGH |
E |
E |
E |
E |
F |
LOW |
20 |
LOW |
|
|
|
CuZn10 |
RED |
44 |
HIGH |
E |
G |
E |
E |
G |
MEDIUM |
20 |
LOW |
|
|
CuZn13 |
RED |
40 |
HIGH |
E |
G |
E |
E |
G |
HIGH |
30 |
LOW |
|
|
CuZn15 |
RED/YELLOW |
37 |
HIGH |
E |
G |
E |
E |
G |
HIGH |
30 |
LOW |
|
|
CuZn20 |
YELLOW |
32 |
LOW |
E |
F |
E |
E |
G |
HIGH |
30 |
LOW |
|
|
CuZn30 |
YELLOW |
28 |
LOW |
E |
F |
E |
E |
F |
VERY HIGH |
30 |
LOW |
|
|
CuZn35 |
YELLOW |
27 |
LOW |
E |
P |
E |
E |
F |
VERY HIGH |
30 |
LOW |
|
|
CuSi2Mn |
COPPER |
12 |
HIGH |
E |
E |
E |
E |
E |
MEDIUM |
30 |
LOW |
|
CuSi3Mn CuSi3Mn |
COPPER |
7 |
VERY HIGH |
E |
E |
G |
E |
E |
VERY HIGH |
30 |
MEDIUM |
*** LOW = H04 TS <
60 ksi; MEDIUM= H04 TS 60-75 ksi;
HIGH= H04 TS 76-100 ksi; VERY HIGH= H04 TS > 100 ksi
Performance
Levels: E = Excellent; G = Good; F =
Fair; P = Poor; NR = Not Recommended